Popular Search:  Tungsten Electrode  |  Mig Electrodes  |  Welding Rods      中文
Home
About Us
Welding Electrodes
Welding Wires
Core Wire
Welding Accessories
Packing
Service & Support
Contact Us
Products blog link
Welding Electrode Manufacturers
Welding Flux
Cast Iron Electrode
Stainless Steel Electrode
Welding Electrode Suppliers
Copper Electrode
Nickel Welding Electrodes
copper brazing alloys
welding cable
mig welding wires
cast iron welding wire
welding alloys
mig electrode
Cast Iron Welding Electrodes
Home > carbon steel welding rod > Points in the welding of carbon steel
Points in the welding of carbon steel
2011-07-26 by seoer

Warm-up warm-up will help reduce the carbon steel heat-affected zone of maximum hardness, prevent cold cracking, which is the main Carbon Steel Welding Rod process measures, but also to improve the joint warm-up plastic, reducing the residual stress after welding. Typically, 35 and 45 steel preheat temperature of 150 ~ 250 ℃ or higher in carbon content due to the thickness and stiffness of large, cracks tend to large, pre-heating temperature can be increased to 250 ~ 400 ℃.

If the weldment is too large, the overall warm-up difficulty, can be partial preheating, the heating range of local warm-up on each side of the weld 150 ~ 200mm.

Electrode preferred alkaline conditions permit electrode.

Groove weldment try to open the form U-shaped groove into the welding-type. If casting defects, shovel dug the groove shape should be smooth, and its aim is to reduce the base metal melt into the weld metal in proportion to reduce the carbon content of the weld, to prevent cracks.

Welding parameters due to the first layer of base metal molten weld metal in the highest proportion of 30%, so the first layer of seam welding, should maximize the use of small current, slow welding speed, to reduce the base metal penetration .

Weld heat treatment after Welding Electrode, welding pieces of the best immediate stress relief heat treatment, especially for the large thickness of the weldments, structural parts and high rigidity under severe conditions (dynamic load or impact load) weldment work and even more so. Eliminate stress tempering temperature 600 ~ 650 ℃.

If post-weld stress relief heat treatment can not be carried out immediately after the heat treatment.

   keywords:    carbon steel welding rod
    nickel alloy welding wire
    mig welding wires
    welding consumables
    welding cable
    welding assembly
    Copper Electrode
    Tungsten Welding Electrode
Copyright 2012-2021 @ Hangzhou Lin'an Dayang Welding Material Co., Ltd. All Right Resrrved          Search engine optimisation and web design by china-webdesign.com