Popular Search:  Tungsten Electrode  |  Mig Electrodes  |  Welding Rods      中文
Home
About Us
Welding Electrodes
Welding Wires
Core Wire
Welding Accessories
Packing
Service & Support
Contact Us
Products blog link
Welding Electrode Manufacturers
Welding Flux
Cast Iron Electrode
Stainless Steel Electrode
Welding Electrode Suppliers
Copper Electrode
Nickel Welding Electrodes
copper brazing alloys
welding cable
mig welding wires
cast iron welding wire
welding alloys
mig electrode
Cast Iron Welding Electrodes
Home > nickel alloy welding wire > Electrode prior to use of custody
Electrode prior to use of custody
2012-03-14 by seoer1

(1) acid electrode is not sensitive to water, organic rutile type Welding Electrode can tolerate higher water content. According to the specific circumstances of the damp, drying

at 70-150 ° for one hour, short storage time and good packing, generally from time to dry before use.

(2) basic low-hydrogen electrodes must be dried before use to reduce the hydrogen content of the electrode, to prevent the pores, cracks and other defects, a general drying

temperature of 350 ° C for one hour. Not be in a furnace electrode suddenly placed in a sudden cooling in order to avoid skin dry. There are special requirements on the

hydrogen content, drying temperature should be raised to 400 ~ 500 ° C, to the amount of hours. Drying the alkaline electrode is best placed in another temperature

controlled at 50 ~ 100 ℃ low temperature drying box, stored and used with the check.

(3) drying electrodes, each Nickel Electrode can not be stacked thick layer (typically 1 to 3) in order to avoid uneven heating in the electrode drying and moisture is not easy to

exclude.

(4) open-air operation, overnight must electrode safekeeping, does not allow open storage should be stored constant temperature in the cold box, otherwise the next day must

be re-dried before use.

   keywords:    nickel alloy welding wire
    nickel alloy welding wire
    mig welding wires
    welding consumables
    welding cable
    welding assembly
    Copper Electrode
    Tungsten Welding Electrode
Copyright 2012-2021 @ Hangzhou Lin'an Dayang Welding Material Co., Ltd. All Right Resrrved          Search engine optimisation and web design by china-webdesign.com