Stainless steel wire can be divided into bits and stainless steel flux cored solid wires .Edit this paragraphStainless steel solid wireStainless steel solid wire with either inert gas welding (TIG, MIG welding ) . Also be used for submerged arc welding . Stainless steel MIG welding can achieve efficient welding , welding automation and easy to implement , widely used in weldingAnd thin pick and other fields. MIG welding with TIG welding wire chemical composition and the same, but for some stainless steel varieties , there is a SI higher Welding Electrodes Manufacturer levels of MIG welding wire, such as with ER308, ER309 wire correspondingER308Si, ER309Si etc., as containing Si up to 0.8 %, and reduces the surface tension of molten metal droplets , the droplet particles become finer, more easily achieved over spray , the arc becomes more stable. While improvingMetal droplet wetting, the weld corrugated appearance, easy to produce Welding Rod Supplier incomplete penetration , slag, porosity and other missing stuffing. Solid wire for submerged arc welding of stainless steel , its chemical composition and the same gas shielded welding stainless steel wire , but it should be equipped withNo fierce silicon fluoride or no fluoride -type low silicon manganese smelting flux.Edit this paragrapStainless steel flux cored wireStainless steel flux cored wire can be as the same as carbon steel and low alloy steel flux cored wire of stainless steel for easy and efficient welding flux cored wire for stainless steel mainly applied to MAG welding , MAG welding is carried out with suchThe following features ; 1 ) compared with manual welding , deposition speed can be increased 2-4 times , and its deposition efficiency up to 90% ( only 55% of the stainless steel electrode ) 2 ) on the current and voltage adaptation range , welding condition setting easier ,Easy to carry semi-automatic and automatic welding . 3 ) good slag , weld surface gloss . In addition , little spatter , excellent arc stability , X-ray passing

A607 electrode E330MoMnWNb-15 DC low hydrogen electrode for 850 ℃ -900 ℃ working under high temperature conditions, the same type of stainless steel materials, welding , and hydrogen furnace manifolds and expansion pipe ( eg Cr20Ni32 andCr20Ni37 material ) weldingA707 electrode low hydrogen Welding Electrodes Manufacturers In China  type DC For acetic acid, vinylon , urea and other welding equipment
A802 welding titanium calcium type AC and DC welding sulfuric acid concentration 50% and a certain temperature and atmospheric pressure in the manufacture of synthetic rubber pipes, and stainless steel welding rod Cr18Ni18Mo2Cu2Ti other instructionsStainless steel electrode can be divided into chromium and chromium -nickel stainless steel welding electrodes, welding of these two who meet the national standard , according to GB GB/T983-1995 assessment