Popular Search:  Tungsten Electrode  |  Mig Electrodes  |  Welding Rods      中文
Home
About Us
Welding Electrodes
Welding Wires
Core Wire
Welding Accessories
Packing
Service & Support
Contact Us
Products blog link
Welding Electrode Manufacturers
Welding Flux
Cast Iron Electrode
Stainless Steel Electrode
Welding Electrode Suppliers
Copper Electrode
Nickel Welding Electrodes
copper brazing alloys
welding cable
mig welding wires
cast iron welding wire
welding alloys
mig electrode
Cast Iron Welding Electrodes
Home > welding consumables > Selection of heat-resistant steel electrode
Selection of heat-resistant steel electrode
2013-09-03 by xiugai
Low-alloy heat-resistant steel at high temperature long-term work, in order to ensure high performance of heat-resistant steel, the steel required to add more of the alloy elements (such as Cr, Mo, V, Nb, etc.). In the choice of welding materials, we must first ensure that the weld and base metal properties matching with the necessary heat resistance, thus requiring the chemical composition of the weld metal and base metal should be consistent. If the weld and base metal chemical composition that much difference, high long-term use, some elements of the joint region diffusion occurs (such as carbon diffusion near the fusion line), the joint trying to performance degradation. Heat-resistant steel electrode can be generally steels and components operating temperature to choose. Optional heat resistant steel Gas Shielded Welding Wire material on the principle that the weld metal alloy composition and performance indicators consistent with the corresponding parent material, or should meet the minimum technical conditions proposed performance indicators. To improve the ability of thermal cracking of the weld metal, the carbon content of the weld should be slightly lower than the carbon content of the base material, should generally be controlled at between 0.07% to 0.15%. Since carbon and alloying elements in steel joint action of heat-resistant Stainless Steel Welding Electrodes can easily form a hardened tissue, weldability is poor. This general preheat heat-resistant steel, tempering after welding. In recent years, thin-walled pipe welding commonly used welding backing, hand acidic surface covered arc welding process, greatly improving the quality of welding. However, the crack resistance of these electrodes is inferior to low hydrogen type electrode, when used alone or when used for welding thick-walled tube, you should choose a low hydrogen type heat-resistant steel electrode.

   keywords:    welding consumables
    nickel alloy welding wire
    mig welding wires
    welding consumables
    welding cable
    welding assembly
    Copper Electrode
    Tungsten Welding Electrode
Copyright 2012-2021 @ Hangzhou Lin'an Dayang Welding Material Co., Ltd. All Right Resrrved          Search engine optimisation and web design by china-webdesign.com