The Carbon Steel Electrode(deposited metal tensile strength less than or equal to 500MPa namely 50kgf/mm2)

applicable to carbon steel and low-strength low alloy steel welding. Low hydrogen, iron powder type electrode before

Welding Electrode  must be baked at 350 ° C above, as far as possible to do with the drying with the use of the

principle of how much baking how much, otherwise it will produce welding defects (such as porosity, slag, cracks,

deterioration of process performance, etc.). Cellulose type electrode should be strictly in accordance with the provisions

of the Manual baking temperature baking, the temperature is too high will burn the cellulose to the drug skin, damage

inherent in the electrode process performance. Using low hydrogen electrodes, the welder should be living in the

upwind position, to enhance ventilation, to prevent the hazards of welding fumes on the body. Low hydrogen type

electrode baking the number of times as much as possible not more than twice to prevent drug skin to become brittle

and fall off.