Popular Search:  Tungsten Electrode  |  Mig Electrodes  |  Welding Rods      中文
Home
About Us
Welding Electrodes
Welding Wires
Core Wire
Welding Accessories
Packing
Service & Support
Contact Us
Products blog link
Welding Electrode Manufacturers
Welding Flux
Cast Iron Electrode
Stainless Steel Electrode
Welding Electrode Suppliers
Copper Electrode
Nickel Welding Electrodes
copper brazing alloys
welding cable
mig welding wires
cast iron welding wire
welding alloys
mig electrode
Cast Iron Welding Electrodes
Home > mig welding rod > Hot forging die repair welding repair process
Hot forging die repair welding repair process
2012-05-18 by seoer8

 

Will be a problem for forging companies, usually a mold 100, the main failure mode of the mold for the wave deformation and crack turtle, and the repair technique can be extended die life savings. The mold base material is mostly 5CrNiMo, 5CrMnMo. Commonly used repair materials GHR397 and 545E, the former more. Hot forging die repair welding repair process as follows:

A weld preparation. Surfacing must first remove the turtle crack, and edge polished into rounded corners, vertical Ying Xiu 100-150 ° slope, resulting in cracks Department should crack all clear, and processed into a V-shaped groove.

2 electrodes, welding machine preparation. Diameter of 4mm GHR397 materials, selection of a DC arc welding machine or Thyristor welder welding, reverse France  Welding Wire  Surfacing current 190-210A, voltage 20-30V is the most suitable.

Electrode drying at 350 ° C, heat 2h, placed in 110-120 ℃ constant temperature.

Mold weld clean-up of the former defect. Cavity defects, machining, carbon arc gouging plus grinding wheel. Cavity parts of the deep, narrow wheel Clear; non-cavity parts, carbon arc gouging clean up.

4 warm-up. Surfacing before the preheating temperature of not less than 400 ° C to prevent weld crack. Motif in the process of welding temperature not less than 300 ° C, slow cooling after welding.

5 Welding Electrode. Using partitions, layered surfacing France, every weld is a weld should immediately remove welding slag and spatter, while the Hammers fast percussion weld to reduce welding stress. The first weld does not knock; the knot between the layers should be staggered. Intermittent welding re-heating is higher than the initial preheating temperature of 40-50 ° C. Transported shall Methods shipped Article swing, swing distance 2.5-3 times the diameter of the electrode.

6 after welding. After welding should be used to heat, slow cold, tempering, annealing. Slow cooling after the grinding processing.

Generally good repair, life expectancy of 90% of the new mold, repair to 1/5 2/3, shorten the production cycle, that is, to repair old, income savings expenditure.

   keywords:    mig welding rod
    nickel alloy welding wire
    mig welding wires
    welding consumables
    welding cable
    welding assembly
    Copper Electrode
    Tungsten Welding Electrode
Copyright 2012-2021 @ Hangzhou Lin'an Dayang Welding Material Co., Ltd. All Right Resrrved          Search engine optimisation and web design by china-webdesign.com